Investigation of the degradation of cellulose acetate museum artefacts

Littlejohn, D., Pethrick, R. A., Quye, A. and Ballany, J. M. (2013) Investigation of the degradation of cellulose acetate museum artefacts. Polymer Degradation and Stability, 98(1), pp. 416-424. (doi:10.1016/j.polymdegradstab.2012.08.023)

Full text not currently available from Enlighten.

Publisher's URL: http://dx.doi.org/10.1016/j.polymdegradstab.2012.08.023

Abstract

Cellulose acetate artefacts from various museums have been analysed by micro-FTIR spectrometry and ion chromatography in an attempt to identify whether there are any common factors associated with their degradation. There was good correlation between the IR spectra, the concentration of ions extracted from an artefact and the visual degree of degradation. Deacetylation, which produced acetate, was found to be the primary process with chain scission (indicated by the appearance of oxalate ion) occurring after degradation is well advanced. Oxidative degradation (indicated by formate) was not a major factor for most artefacts studied, however the loss of formate by volatilization cannot be excluded. Changes to the polymer matrix as a consequence of degradation were indicated in some artefacts by the presence of plasticiser on the surface and increased levels of extractable chloride and/or sulphate.<p></p> A simple test of the onset of degradation was developed that involved analysis of an aqueous swab of the surface of an artefact by ion chromatography. Analysis by X-ray fluorescence spectrometry allowed identification of selenium as a potential stabilizing element in certain areas of a doll which were less degraded than other parts that had no selenium.<p></p>

Item Type:Articles
Status:Published
Refereed:Yes
Glasgow Author(s) Enlighten ID:Quye, Dr Anita
Authors: Littlejohn, D., Pethrick, R. A., Quye, A., and Ballany, J. M.
College/School:College of Arts > School of Culture and Creative Arts > History of Art
Journal Name:Polymer Degradation and Stability
Publisher:Elsevier
ISSN:0141-3910
ISSN (Online):1873-2321

University Staff: Request a correction | Enlighten Editors: Update this record